PA66 47H美國首諾Vydyne®通用級沖擊改性尼龍66塑料（18024445500）

Physical Dry Conditioned Unit Test Method
Density 1.10　-- g/cm³ ISO 1183
Molding Shrinkage 　 　 　 ISO 294-4
Across Flow : 23°C, 2.00 mm 1.6　-- % 　
Flow : 23°C, 2.00 mm 1.8　-- % 　
Water Absorption (23°C, 24 hr) 1.2　-- % ISO 62
WaterAbsorption (Equilibrium, 23°C, 50% RH) 2.3　-- % ISO 62
Tensile Modulus (23°C) 2780　1740　MPa ISO 527-2
Tensile Stress (Yield, 23°C) 60.0　45.0　MPa ISO 527-2
Tensile Stress (Break, 23°C) 52.0　40.0　MPa ISO 527-2
Tensile Strain (Break, 23°C) 22　60　% ISO 527-2
Flexural Modulus (23°C) 2300　780　MPa ISO 178
Flexural Stress (23°C) 70.0　24.0　MPa ISO 178
Impact Dry Conditioned Unit Test Method
Charpy Notched Impact Strength 　 　 　 ISO 179
-40°C 11　18　kJ/m² 　
-30°C 17　24　kJ/m² 　
23°C 19　62　kJ/m² 　
Charpy Unnotched Impact Strength 　 　 　 ISO 179
-30°C No Break No Break　 　
23°C No Break No Break　 　
Notched Izod Impact Strength 　 　 　 ISO 180
-40°C 12　18　kJ/m² 　
-30°C 16　24　kJ/m² 　
23°C 18　44　kJ/m² 　
Heat Deflection Temperature 　 　 　 ISO 75-2/B
0.45 MPa, Unannealed 185　-- °C 　
Heat Deflection Temperature 　 　 　 ISO 75-2/A
1.8 MPa, Unannealed 63.0　-- °C 　
Melting Temperature 260　-- °C ISO 11357-3
CLTE - Flow (23 to 55°C, 2.00 mm) 　 -- cm/cm/°C ISO 11359-2
CLTE - Transverse (23 to 55°C, 2.00 mm) 　 -- cm/cm/°C ISO 11359-2
RTI Elec 　 　 　 UL 746
0.750 mm 130　-- °C 　
1.50 mm 130　-- °C 　
3.00 mm 130　-- °C 　
RTI Imp 　 　 　 UL 746
0.750 mm 75.0　-- °C 　
1.50 mm 75.0　-- °C 　
3.00 mm 75.0　-- °C 　
RTI Str 　 　 　 UL 746
0.750 mm 115　-- °C 　
1.50 mm 115　-- °C 　
3.00 mm 115　-- °C 　
Electrical Dry Conditioned Unit Test Method
Volume Resistivity (0.750 mm) 　 -- ohm·cm IEC 60093
Dielectric Strength (1.00 mm) 12　-- kV/mm IEC 60243
Arc Resistance PLC 6 --　 ASTM D495
Comparative Tracking Index (3.00 mm) 525　-- V IEC 60112
High Amp Arc Ignition (HAI) 　 　 　 UL 746
0.750 mm PLC 0 --　 　
1.50 mm PLC 0 --　 　
3.00 mm PLC 0 --　 　
High Voltage Arc Tracking Rate (HVTR) PLC 2 --　 UL 746
Hot-wire Ignition (HWI) 　 　 　 UL 746
0.750 mm PLC 4 --　 　
1.50 mm PLC 4 --　 　
3.00 mm PLC 3 --　 　
Flame Rating 　 　 　 UL 94
0.750 mm HB --　 　
1.50 mm HB --　 　
3.00 mm HB --　 　
Glow Wire Flammability Index 　 　 　 IEC 60695-2-12
0.750 mm 700　-- °C 　
1.50 mm 775　-- °C 　
3.00 mm 700　-- °C 　
Glow Wire Ignition Temperature 　 　 　 IEC 60695-2-13
0.750 mm 725　-- °C 　
1.50 mm 800　-- °C 　
3.00 mm 725　-- °C 　
Injection 　 Dry Unit 　 　
Drying Temperature 　 80.0 °C 　　
Drying Time 　 4.0 hr 　　
Suggested Max Regrind 　 25 % 　　
Rear Temperature 　 280 to 310 °C 　　
Middle Temperature 　 280 to 310 °C 　　
Front Temperature 　 280 to 310 °C 　　
Nozzle Temperature 　 280 to 310 °C 　　
Processing (Melt) Temp 　 285 to 305 °C 　　
Mold Temperature 　 65.0 to 95.0 °C