PA6 BKV 30 G H2.0 900051德國朗盛Durethan 30%玻纖增強尼龍6塑料（18024445500）

PA 6, 30 % glass fibers, injection molding, heat-aging stabilized, improved surface finish, improved resistance to weathering

ISO/ ASTM

ISO Shortname: ISO 1874-PA 6, GHR, 14-100, GF30

Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.27　
C Molding shrinkage, transverse 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.58　
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.06　
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.16　

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 10000 6200
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 180 110
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 3.0 7.0
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 75 75
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 60 60
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA 10 13
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA < 10 < 10
Charpy notched impact strength -40 °C kJ/m² ISO 179-1eA < 10 < 10
Izod impact strength 23 °C kJ/m² ISO 180-1U 65 70
Izod impact strength -30 °C kJ/m² ISO 180-1U 55 55
Izod notched impact strength -30 °C kJ/m² ISO 180-1A < 10 <10
Izod notched impact strength -40 °C kJ/m² ISO 180-1A < 10 <10
Flexural modulus 2 mm/min MPa ISO 178-A 9300 5700