PA6 C 50H2 NATURAL法國羅地亞TECHNYL阻燃高延展性注塑擠出尼龍6塑料（18024445500）

　 Standards Unit Values 　
　 　 　 d.a.m. Cond.
Physical 　 　 　 　
Water absorption(24h at 23°C) ISO 62 % 1,10 　
Density ISO 1183/A g/cm3 1,16 　
Molding shrinkage Parallel RHODIA % 1,30 　
Molding shrinkage normal or perpendicular RHODIA % 0,80 　
Mechanical 　 　 　 　
Tensile Modulus ISO 527 Type 1A MPa 3500　2000　
Tensile strength at yield ASTM D-638 MPa 80　　
　 ISO 527 Type 1A MPa 75　50　
Tensile strength at break ISO 527 Type 1A MPa 60　40　
　 ASTM D-638 MPa 80　　
Elongation at yield ISO 527 Type 1A % 3,50 5　
Elongation at break ISO 527 Type 1A % 25　38　
　 ASTM D-638 % 15　　
Flexural modulus ISO 178 MPa 3150　2000　
　 ASTM D-790 MPa 3500　　
Flexural maximum stress ISO 178 MPa 200　70　
　 ASTM D-790 MPa 115　　
Charpy notched impact strength (23 °C) ISO 179/1eA kJ/m2 6　15　
Charpy unnotched impact strength (23 °C) ISO 179/1eU kJ/m2 180　　
Izod notched impact strength (23 °C) ISO 180/1A kJ/m2 3,5 15　
　 ASTM D256 J/m 65