Physical Dry Conditioned Unit Test Method
Density 1.50 -- g/cm³ ISO 1183
Molding Shrinkage ISO 294-4
Across Flow 23°C, 2.00 mm 0.90 -- %
Flow 23°C, 2.00 mm 0.40 -- %
Water Absorption 23°C, 24 hr 0.60 -- % ISO 62
WaterAbsorption Equilibrium, 23°C, 50% RH 1.5 -- % ISO 62
Mechanical Dry Cond...
PA66 R860 BK02美國首諾Vydyne玻纖礦物增強尼龍66塑料 PA66 R860 BK02美國首諾Vydyne玻纖礦物增強尼龍66塑料18024445500
Mechanical Dry Conditioned Unit Test Method
Tensile Modulus 23°C 10000 5900 MPa ISO 527-2
Tensile Stress Break, 23°C 120 90.0 MPa ISO 527-2
Tensile Strain Break, 23°C 2.5 2.8 % ISO 527-2
Flexural Modulus 23°C 9000 4500 MPa ISO 178
PA66 PA66-AF35-02-US美國泰科納CELSTRAN 35%芳族聚酰胺纖維 PA66 PA66-AF35-02-US美國泰科納CELSTRAN 35%芳族聚酰胺纖維18024445500
PA66 with 35% aramid fiber by weight
Physical properties Value Unit Test Standard
Density 1220 kg/m³ ISO 1183
Mechanical properties Value Unit Test Standard
Tensile modulus 1mm/min 9200 MPa ISO 527-2/1A
Tensile stress at break 5mm/min 120 MPa ISO 527-2/1A
Tensile strain at break 5mm/min 1.86 % ISO...
PA66 PA66-CF40-02 AF3004 Natural美國泰科納CELSTRAN 40%長碳纖 PA66 PA66-CF40-02 AF3004 Natural美國泰科納CELSTRAN 40%長碳纖維增強18024445500
40% long carbon fiber reinforced Nylon 6/6
Physical properties Value Unit Test Standard
Density 1340 kg/m³ ISO 1183
Mold shrinkage - parallel 0.0005 % ISO 294-4
Mold shrinkage - normal 0.003 % ISO 294-4
PA66 PA66-GF20-02P11/12美國泰科納CELSTRAN 20%長玻纖增強尼龍6 PA66 PA66-GF20-02P11/12美國泰科納CELSTRAN 20%長玻纖增強尼龍66塑料18024445500
Physical properties Value Unit Test Standard
Density 1300 kg/m³ ISO 1183
Mechanical properties Value Unit Test Standard
Tensile modulus 1mm/min 8300 MPa ISO 527-2/1A
Tensile modulus 80°C 4970 MPa ISO 527-2/1A
Tensile strength 80°C 103 MPa ISO 527-2/1A